| Name | Epoxy Resin Insulation Raw Material For Electrical Components And Products Bushing And Busbar |
|---|---|
| Curing Time | 80°C×4 Hrs+140°C*12hrs |
| Epoxy / Hardener Mixture Temperature | 50-60°C /1-1.5hours |
| Gelation Time | 80°C/4 Hrs+100°C/2hrs+120°C/2hrs. |
| Impact Strength | 8-16kJ / M2 |
| Name | Electrical Epoxy Resin |
|---|---|
| Curing Time | 130-140°C×6-10 Hrs. |
| Epoxy / Hardener Mixture Temperature | 50-60°C /1-1.5hours |
| Gelation Time | 80°C/4 Hrs+100°C/2hrs+120°C/2hrs. |
| Flammability | HB Class |
| Cure Temperature | 130-140℃ |
|---|---|
| Color/Appearance | ISO12058 Light Yellow-colorless Liquid |
| Compressive Strength | ISO604 150-200N/ Mm2 |
| Impact Strength | ISO179 10-18kJ/ M2 |
| Tg (DSC) | ISO11357-2 100-120℃ |
| Color | Transparent, Light Yellow, Viscous Liquid |
|---|---|
| Curing Time | 130-140°C×6-10 Hrs. |
| Dielectric Strength | 20-30kV / Mm |
| Elongation | High |
| Flammability | HB Class |
| Tg (DSC) | ISO11357-2 100-120℃ |
|---|---|
| Cure Temperature | 130-140℃ |
| Flexural Strength | ISO178 110-140N/ Mm2 |
| Compressive Strength | ISO604 150-200N/ Mm2 |
| Cure Shrinkage | ISO178 0.6-0.8% |
| Flexural Strength | ISO178 110-140N/ Mm2 |
|---|---|
| Loss Factor | 0.02 |
| Compressive Strength | ISO604 150-200N/ Mm2 |
| Density At 25℃ | ISO1675 1.16-1.2 |
| Cure Shrinkage | ISO178 0.6-0.8% |
| Process | APG |
|---|---|
| Color | Light Yellow |
| Material | YD-128 RESIN |
| Machine | Casting And Oven |
| Certificate | CE |
| Classification | Double Components Adhesives |
|---|---|
| Usage | Electrical Insulation |
| Main Raw Material | Epoxy |
| Type | Epoxy Resin Compound |
| Material | Epoxy |
| Classification | Double Components Adhesives |
|---|---|
| Usage | Electrical Insulation |
| Main Raw Material | Epoxy |
| Type | Epoxy Resin Compound |
| Material | Epoxy |
| Classification | Double Components Adhesives |
|---|---|
| Usage | Electrical Insulation |
| Main Raw Material | Epoxy |
| Type | Epoxy Resin Compound |
| Material | Epoxy |